DRAM capacitor formulation using a double-sided electrode

ABSTRACT

A capacitor having a double sided electrode for enhanced capacitance. In one embodiment, the double sided electrode capacitor is a stacked container capacitor used in a dynamic random access memory circuit. The double sided electrode is preferably formed of a conductive metal, provided that an oxide of the metal is conductive. The double sided electrode capacitor provides a capacitor that has high storage capacitance which provides an increased efficiency for a cell without an increase in the size of the cell.

This application is a continuation of application Ser. No. 09/415,213, filed Oct. 12, 1999 now U.S. Pat. No. 6,451,661 which is a divisional of application Ser. No. 09/089,445, filed on Jun. 3, 1998, both of which are hereby incorporated by reference.

FIELD OF THE INVENTION

The invention relates generally to integrated circuits and more particularly to a double sided lower electrode capacitor for use in an integrated circuit.

BACKGROUND OF THE INVENTION

Capacitors are used in a wide variety of semiconductor circuits. Capacitors are of special concern in DRAM (dynamic random access memory) memory circuits; therefore, the invention will be discussed in connection with DRAM memory circuits. However, the invention has broader applicability and is not limited to DRAM memory circuits. It may be used in any other type of memory circuit, such as an SRAM (static random access memory), as well as in any other circuit in which capacitors are used.

DRAM memory circuits are manufactured by replicating millions of identical circuit elements, known as DRAM cells, on a single semiconductor wafer. A DRAM cell is an addressable location that can store one bit (binary digit) of data. In its most common form, a DRAM cell consists of two circuit components: a storage capacitor and an access field effect transistor.

FIG. 1 illustrates a portion of a DRAM memory circuit containing two neighboring DRAM cells 10. For each cell, one side of the storage capacitor 14 is connected to a reference voltage, which is typically one half of the internal operating voltage (the voltage corresponding to a logical “1” signal) of the circuit. The other side of the storage capacitor 14 is connected to the drain of the access field effect transistor 12. The gate of the access field effect transistor 12 is connected to a signal referred to as the word line 18. The source of the field effect transistor 12 is connected to a signal referred to as the bit line 16. With the circuit connected in this manner, it is apparent that the word line controls access to the storage capacitor 14 by allowing or preventing the signal (a logic “0” or a logic “1”) on the bit line 16 to be written to or read from the storage capacitor 14.

The manufacturing of a DRAM cell includes the fabrication of a transistor, a capacitor, and three contacts: one each to the bit line, the word line, and the reference voltage. DRAM manufacturing is a highly competitive business. There is continuous pressure to decrease the size of individual cells and increase memory cell density to allow more memory to be squeezed onto a single memory chip. However, it is necessary to maintain a sufficiently high storage capacitance to maintain a charge at the refresh rates currently in use even as cell size continues to shrink. This requirement has led DRAM manufacturers to turn to three dimensional capacitor designs, including trench and stacked capacitors. Stacked capacitors are capacitors which are stacked, or placed, over the access transistor in a semiconductor device. In contrast, trench capacitors are formed in the wafer substrate beneath the transistor. For reasons including ease of fabrication and increased capacitance, most manufacturers of DRAMs larger than 4 Megabits use stacked capacitors. Therefore, the invention will be discussed in connection with stacked capacitors but should not be understood to be limited thereto. For example, use of the invention in trench or planar capacitors is also possible.

One widely used type of stacked capacitor is known as a container capacitor. Known container capacitors are in the shape of an upstanding tube (cylinder) having an oval or circular cross section. FIG. 2 illustrates a top view of a portion of a DRAM memory circuit from which the upper layers have been removed to reveal container capacitors 14 arranged around a bit line contact 16. Six container capacitors 14 are shown in FIG. 2, each of which has been labeled with separate reference designations A to F. Recall from FIG. 1 that the bit lines of neighboring DRAM cells are electrically connected. To increase density, bit line contacts are shared by neighboring DRAM cells. In FIG. 2, the bit line contact 16 is shared by DRAM cells corresponding to container capacitors A and B. The wall of each tube consists of two plates of conductive material such as doped polycrystalline silicon (referred to herein as polysilicon or poly) separated by a dielectric. A preferred dielectric is tantalum pentoxide (Ta₂O₅). The bottom end of the tube is closed, with the outer wall in contact with either the drain of the access transistor or a plug which itself is in contact with the drain. The other end of the tube is open (the tube is filled with an insulative material later in the fabrication process). The sidewall and closed end of the tube form a container; hence the name “container capacitor.” Although the invention will be further discussed in connection with stacked container capacitors, the invention should not be understood to be limited thereto.

The electrodes in a DRAM cell capacitor must be conductive, and must protect the dielectric film from interaction with interlayer dielectrics (e.g., BPSG) and from the harsh thermal processing encountered in subsequent steps of DRAM process flow. For example, Ta₂O₅ dielectrics may be used for high density DRAMs, such as 64 Mbit and 256 Mbit DRAMs, because chemical vapor deposition (CVD) of Ta₂O₅ provides a high dielectric constant (about 20-25) and good step coverage. However, when rapid thermal processed nitride (RTN) is formed over a layer of hemispherical grain polysilicon (HSG) to serve as an HSG barrier layer to prevent oxidation of HSG during subsequent Ta₂O₅ deposition, there is a capacitance loss due to the RTN layer on the capacitor electrode. The effective dielectric constant for an RTN/Ta₂O₅ stack capacitor is about 10-12.

Several methods have been attempted to increase capacitance, including depositing HSG inside a container capacitor together with a smooth polysilicon deposited on the outside of the container, depositing a smooth metal on both the inside and outside of the capacitor, and depositing a double sided HSG. The present invention has advantages over the previous methods in that the HSG inside with smooth polysilicon outside capacitors, and the smooth metal capacitors, have lower capacitance and do not achieve the superior results of the present invention. Regarding the double sided HSG capacitor, the present invention also overcomes the difficulties involved in using HSG on the outside of a capacitor plate, and the resulting in short circuits between containers and defects in the capacitor.

As memory cell density continues to increase, there is needed a capacitor that has an increased effective capacitance per cell. The present invention provides a fabrication process and capacitor structure that achieves high storage capacitance without increasing the frequency of capacitor defects or the size of the capacitor.

SUMMARY OF THE INVENTION

The present invention provides a double sided electrode capacitor formed of a metal electrode that preferably has an additional conductive layer, preferably HSG, on one side, together with a silica nitride coating dielectric, and a dielectric material such as Ta₂O₅ on another side, as shown, for example, in FIG. 3.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a circuit diagram of a portion of a conventional DRAM memory circuit.

FIG. 2 is a top view of a cross section of a known memory circuit showing a number of conventionally shaped container capacitors surrounding a bit line contact.

FIG. 3A is top view of a partially cut away cross section of one embodiment of a memory circuit according to the present invention showing a double sided lower electrode capacitor according to the invention.

FIG. 3B is a side view of the cross section of FIG. 3A.

FIG. 4 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at an early processing step according to one embodiment of the present invention.

FIG. 5 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 4.

FIG. 6 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 5.

FIG. 7 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 6.

FIG. 8 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 7.

FIG. 9 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 8.

FIG. 10 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 9.

FIG. 11 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 10.

FIG. 12 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 11.

FIG. 13 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 12.

FIG. 14 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 13.

FIG. 15 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 14.

FIG. 16 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 15.

FIG. 17 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 16.

FIG. 18 is a diagrammatic cross-sectional view of a portion of a semiconductor wafer at a processing step subsequent to that shown in FIG. 17.

FIG. 19 is a cross section of another embodiment of the invention having a barrier layer between the plug and the lower electrode of the capacitor.

FIG. 20 is a block diagram of a computer system comprising a memory including a double sided capacitor.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

An exemplary construction of a fabrication process for a container capacitor according to one embodiment of the present invention is described below. It is to be understood, however, that this process is only one example of many possible processes. For example, the bit line is formed over the capacitor in the following process. A buried bit-line process could also be used. As another example, the plugs under the capacitors formed by the following process could be eliminated. Also, dry or wet etching could be used rather than chemical mechanical polishing. The invention is not intended to be limited by the particular process described below.

Referring now to FIG. 4, a semiconductor wafer fragment at an early processing step is indicated generally by reference numeral 100. The semiconductor wafer 100 is comprised of a bulk silicon substrate 112 with field isolation oxide regions 114 and active areas 116, 118, 120 formed therein. Word lines 122, 124, 126, 128 have been constructed on the wafer 100 in a conventional manner. Each word line consists of a lower gate oxide 130, a lower poly layer 132, a higher conductivity silicide layer 134 and an insulating silicon nitride cap 136. Each word line has also been provided with insulating spacers 138, which are also composed of silicon nitride.

Two FETs are depicted in FIG. 4. One FET is comprised of two active areas (source/drain) 116, 118 and one word line (gate) 124. The second FET is comprised of two active areas (source/drain) 118, 120 and a second word line (gate) 126. The active area 118 common to both FETs is the active area over which a bit line contact will be formed. As discussed above, one bit line contact is shared by two DRAM cells to conserve space.

Referring now to FIG. 5, a thin layer 140 of nitride or TEOS (tetraethyl orthosilicate) is then provided atop the wafer 100. Next a layer of insulating material 142 is deposited. The insulating material preferably consists of borophosphosilicate glass (BPSG). The insulating layer 142 is subsequently planarized by chemical-mechanical polishing (CMP).

Referring now to FIG. 6, plug openings have been formed through the insulating layer 142. The plug openings 144 are formed through the insulating layer 142 by photomasking and dry chemical etching the BPSG relative to the thin nitride layer 140. Referring now to FIG. 7, a layer 146 of conductive material is deposited to provide conductive material within the plug openings 144. The conductive plug layer 146 is in contact with the active areas 116, 118, 120. An example of the material used to form conductive plug layer 146 is in situ arsenic or phosphorous doped poly. Referring now to FIG. 8, the conductive plug layer 146 is dry etched (or chemical-mechanical polished) to a point just below the upper surface of the BPSG layer 142 such that the remaining material of the conductive plug layer 146 forms electrically isolated plugs 146 over the active areas 116, 118, 120. In another embodiment, conventional electrode materials may be used and then provided with a barrier layer atop the electrode, or between the electrode and the dielectric, or in both locations. This embodiment is described further below with reference to FIG. 19.

Still with reference to FIG. 8, an additional layer 148 of BPSG is then deposited on the structure. Referring now to FIG. 9, capacitor openings 150 are then formed in the BPSG layer 148 by photomasking and dry chemical etching. The height of the plugs, as defined by the conductive plug layer 146 over the non-bit line active areas 116, 120 is also reduced by this step.

Referring now to FIG. 10, a conductive layer 152 of conductive material that will eventually form the double sided electrode of the capacitor is deposited at a thickness such that the capacitor openings 150 are not closed off. The term double sided electrode, as used herein, shall be understood to mean an electrode having at least two sides that emit, collect or deflect electric charge carriers, and which, at each of its two sides, opposes a corresponding electrode with a dielectric material disposed between each side of the double sided electrode and a corresponding electrode. The term dielectric is used herein shall be understood to mean any solid, liquid or gaseous material that can sustain an electrical field for use in the capacitor of a DRAM cell or other integrated circuit device containing a capacitor.

The conductive layer 152 may be formed of a Ruthenium (Ru) layer to increase capacitance. The only requirement for the selection of the conductive layer 152 is that the metal or alloy form an oxide that is also conductive. Non-limiting examples of materials that may be used to form the conductive layer 152 are RuO₂, Ir, IrO₂, Ta, Rh, RhO_(x), VO₃, and alloys, such as Pt—Ru or Pt—Rh. The conductive layer 152 may be deposited onto the insulating layer 142 by CVD, LPCVD, PECVD, MOCVD, sputtering or other suitable deposition techniques.

If Ru is used as the conductive layer 152, the conductive layer 152 may be formed by first depositing a layer of Ru over the insulating layer 142 by chemical vapor deposition (CVD) or any other conformal process. Preferably the conductive layer 152 has a thickness of about 100 to about 1000 Angstroms, more preferably less than 500 Angstroms.

Referring to FIG. 11, a capacitance layer 153 is deposited over the conductive layer 152. The capacitance layer 153 may also be formed of HSG (hemispherical grained poly), silica, silicon, germanium or an alloy of silica or germanium to increase capacitance. Preferably the capacitance layer 153 is formed of HSG (hemispherical grained poly). If HSG is used, the capacitance layer 153 may be formed by first depositing a layer of in situ doped polysilicon followed by a deposition of undoped HSG. Subsequent heating inherent in wafer processing will effectively conductively dope the overlying HSG layer. Alternatively, the capacitance layer 153 may be provided by in situ arsenic doping of an entire HSG layer or the capacitance layer 153 may be formed by depositing amorphous silicon at this step and then using a selective seed followed by an annealing process and chemical mechanical polishing. The conductive layer 152 and the capacitance layer 153 are in electrical contact with the previously formed plugs 146 over the non-bit line active areas 116, 120.

Referring now to FIG. 12, the portions of the conductive layer 152 and the capacitance layer 153 above the top of the second BPSG layer 148 are removed through a CMP or etching process, thereby electrically isolating the portions of conductive layer 152 and the capacitance layer 153 remaining in the capacitor openings 150.

Referring now to FIG. 13, a dielectric film layer 155 is formed over the surface of capacitance layer 153. The preferred dielectric film is a nitride film and though this nitride film may be formed using various methods, it is preferred to use rapid thermal nitridation (RTN) processing at a temperature ranging from about 600° C. to about 1200° C., preferably between 800° C. and 1000° C. for a time period ranging from about 5 seconds to about 60 seconds, preferably from about 20 seconds to about 60 seconds. The nitride film of the dielectric film layer 155 is formed using RTN in the presence of NH₃, hydrazine, an ammonia plasma, or other nitrogen sources in order to form a nitride layer on the capacitance layer 153. The dielectric film layer 155 preferably has a thickness of from about 10 to about 50 Angstroms, more preferably from about 15 to about 30 Angstroms.

Referring now to FIG. 14, the insulating layer 142, which is preferably formed of BPSG, and the BPSG layer 148, are then etched back around the conductive layer 152, in order to expose the conductive layer 152. The insulating layer 142 and the BPSG layer 148 are preferably removed by the use of an etchant containing a dilute solution of hydrofluoric acid (HF), such as a 10:1 volumetric ratio of water to 49% HF solution; however, the invention is not limited to this particular etchant. Any method of exposing conductive layer 152 or of removing the insulating layer 142 and the BPSG layer 148 from around the conductive layer 152 is within the scope of the present invention.

Referring now to FIG. 15, dielectric layer 157 is deposited over the remaining insulating layer 142, the exposed portion of the conductive layer 152, the BPSG layer 148, and the dielectric film layer 155. The dielectric layer 157 is preferably deposited such that the capacitor openings 150 are not filled. The dielectric layer 157 may be formed from dielectric materials such as: Ta₂O₅, SrTiO₃, Y₂O₃, Nb₂O₅, ZrO₂, titanium oxide or the like. Preferably, the dielectric layer 157 is Ta₂O₅. The dielectric layer 157 may be deposited by a low-pressure CVD process using Ta(OC₂H₅)₅ and O₂ at about 430° C., and may be subsequently annealed in order to reduce leakage current characteristics.

Referring now to FIG. 16, a second conductive layer 156 is deposited to form the corresponding electrode over the dielectric layer 157, again at a thickness which less than completely fills the bit line contact and capacitor openings 150, 146. The second conductive layer 156 is preferably composed of titanium nitride. A poly silicon layer (not shown) may be coated over the second conductive layer 156. It should be understood that the second conductive layer 156 may be formed of any conductive material. In addition to serving as the second plate or corresponding electrode of the capacitor, the second conductive layer 156 also forms the interconnection lines between the second plates of the capacitors. The second plate of the capacitor is connected to the reference voltage, as discussed above in connection with FIG. 1.

Referring now to FIG. 17, the second conductive layer 156 and underlying capacitor dielectric layers are patterned and etched such that the remaining portions of the dielectric layer 157 and second conductive layer 156 over each capacitor opening 150 are electrically isolated from one another. In this manner, each of the active areas 116, 118, 120 are also electrically isolated (without the influence of the gate).

Referring now to FIG. 18, a bit line insulating layer 158 is provided over the second conductive layer 156 and the second BPSG layer 148. The bit line insulating layer 158 may be comprised of BPSG, PSG, flowable glass, spun glass or other insulative material. Preferably the bit line insulating layer 158 is BPSG. A bit line contact opening 160 is patterned through the bit line insulating layer 158 such that the conductive plug layer 146 is once again outwardly exposed. Then a bit line contact is provided in the bit line contact opening 160 such that the bit line contact is in electrical contact with the outwardly exposed portion of the plug 146. Thus, the outwardly exposed portion of the plug 146 over the active area 118 common to both FETs acts as a bit line contact.

FIG. 19 illustrates another embodiment of the double sided electrode capacitor of the invention. As can be seen from this figure, a barrier layer 160 is formed between the conductive layer 152, which forms the double sided electrode of the capacitor, and the conductive plug layer 146. The barrier layer 160 according to the invention may be comprised of materials that have excellent conductivity and the ability to reduce depletion effects and enhance frequency response. The barrier layer materials also possess excellent barrier properties for protection of cell dielectrics during BPSG reflow and other high temperature steps after capacitor formation, and also prevent the diffusion of silicon and oxygen into the cell. Suitable barrier layer materials are, for example, titanium nitride, aluminum nitride, titanium boride, zirconium boride and hafnium boride. The barrier layer 160 may be as thin as 50 to 300 Angstroms and still improve conduction, reduce migration of silicon into the cell, and reduce oxidation of the cell.

FIG. 20 illustrates a computer system 300 according to one embodiment of the present invention. The computer system 300 comprises a CPU (central processing unit) 302, a memory circuit 304, and an I/O (input/output) device 306. The memory circuit 304 contains a DRAM memory circuit including the capacitors according to the present invention. Memory other than DRAM may be used. Also, the CPU itself may be an integrated processor which utilizes integrated capacitors according to the present invention.

The advantages of the capacitors in accordance with the present invention will now be discussed in further detail with reference to FIGS. 3A and 3B. As noted, FIG. 3A shows a top view of a capacitor from which the upper layers have been removed to reveal the container capacitor 15. The capacitor 15 has a double sided lower electrode 152 which is in electrical contact with the plug 146 as shown in FIG. 3B. The lower electrode is formed of a conductive layer 152. As noted in the figures, on one side of the lower electrode 152 of the capacitor 15, there is a capacitance layer 153, preferably formed of HSG. Atop the capacitance layer 153 is a dielectric film layer 155. Preferably, the dielectric film layer 155 is formed of a nitride film through an RTN process. Atop the dielectric film layer 155, and also on the other side of the lower electrode 152, are dielectric layers 157. Preferably the dielectric layer 157 is comprised of Ta₂O₅. It should be noted, as set forth in the drawings, that there is no dielectric film layer 155 on the non-capacitance layer (HSG) side of the lower electrode 152.

The result of such a structure is that the effective dielectric constant of the dielectric layer 157 on the outside of the capacitor 15 will be high, for example, about 20 to 25 for Ta₂O₅ as the dielectric. This is due to the double sided lower electrode and the lack of RTN in series with the dielectric layer 157 on the outside of the capacitor. The effective dielectric constant of the dielectric layer 157 over the dielectric film layer 155 and the capacitance layer 153 is between about 10 and about 12. Thus, the capacitance per area (C/A) will be more than 17 fF/μm² for the outside of the capacitor 15, and more than 24 fF/μm² for the inside of the capacitor 15, due to the surface area of the inside of the capacitor and the fabrication of the capacitor as described above.

Thus, for example, for a 0.18 DRAM cell, the surface area of the outside of the capacitor is about 1 μm² for 1 μm tall containers fully etched back. By using the preferred capacitor of the present invention, the capacitor would have an increase of more than 7 fF/μm² per cell over previous HSG inside/smooth polysilicon outside capacitors. This results in approximately a 1.8 times capacitance enhancement factor for the outside of the capacitor compared to previous structures. The present invention provides an increased effective capacitance and a high capacitance per cell. The present invention also provides a capacitor that has high storage capacitance without increasing the size of the capacitor. The present invention also enables an increased efficiency for the cell without a corresponding increase in the size of the cell.

It should again be noted that although the invention has been described with specific reference to DRAM memory circuits and container capacitors, the invention has broader applicability and may be used in any integrated circuit requiring capacitors. Similarly, the process described above is but one method of many that could be used. Accordingly, the above description and accompanying drawings are only illustrative of preferred embodiments which can achieve and provide the objects, features and advantages of the present invention. It is not intended that the invention be limited to the embodiments shown and described in detail herein. The invention is only limited by the spirit and scope of the following claims. 

What is claimed as new and desired to be protected by Letters Patent of the United States is:
 1. A method of forming a memory cell comprising the steps of forming a transistor including a source and a dram over an active area of a substrate, wherein said source of said transistor is connected to a bit line and a gate of said transistor is connected to a word line; and forming a capacitor connected to said drain of said transistor and to a voltage reference, wherein said step of forming said capacitor further comprises forming a first conductive layer as a double sided electrode having an inner side and an outer side, said outer side being adjacent to at least one insulating layer; forming a first dielectric layer over the inner side of the double sided electrode; exposing at least a portion of the at least one insulating layer on the outer sided electrode to form an exposed portion of said double sided electrode; forming a second dielectric layer over said first dielectric layer and said exposed portion of said double sided electrode; and forming a second conductive layer over said second dielectric layer.
 2. The method of claim 1, wherein said first conductive layer is formed of a metal, wherein an oxide of said metal is conductive.
 3. The method of claim 1, wherein said first conductive layer is formed of a material selected from the group consisting of Ru, RuO₂, Ir, IrO₂, Ta, Rh, RhO_(x), VO₃, a Pt—Ru alloy and a Pt—Rh alloy.
 4. The method of claim 1 further comprising forming a barrier layer in contact with and beneath at least a portion of said first conductive layer.
 5. The method of claim 1, wherein said second conductive layer is formed of a material selected from the group consisting of hemispherical grained polysilicon, silica, silicon, germanium and alloys of silica and germanium.
 6. The method of claim 1 further comprising forming a third conductive layer between said first conductive layer and said first dielectric layer.
 7. The method of claim 6, wherein said third conductive layer is formed of a material selected from the group consisting of hemispherical grained polysilicon, silica, silicon, germanium and alloys of silica and germanium.
 8. The method of claim 1, wherein said first dielectric layer is a nitride film formed by rapid thermal nitridation (RTN).
 9. The method of claim 1, wherein said second dielectric layer is formed of a material selected from the group consisting of Ta₂O₅, SrTiO₃, Y₂O₃, Nb₂O₅, ZrO₂ and TiO_(x).
 10. The method of claim 1, wherein said memory cell is a DRAM memory cell.
 11. A method of forming a pair of memory cells connected to a common bit line, said method comprising the steps of: forming respective transistors corresponding to said pair of memory cells, each of said respective transistors including a source and a drain over an active area of a substrate, wherein said source of each of said respective transistors is connected to a bit line and a gate of each of said respective transistors is connected to a word line; and forming respective capacitors corresponding to said respective transistors, wherein each of said respective capacitors is connected to said drain of each of said respective transistors and to a voltage reverence, wherein said step of forming each of said respective capacitors further comprises forming a first conductive layer as a double sided electrode having an inner side and an outer side, said outer side being adjacent to at least one insulating layer; forming a first dielectric layer over the inner side of the double sided electrode; exposing at least a portion of the at least one insulating layer on the outer side of said first conductive layer to form an exposed portion of said double sided electrode; forming a second dielectric layer over said first dielectric layer and said exposed portion of said double sided electrode; and forming a second conductive layer over said second dielectric layer.
 12. The method of claim 11, wherein said first conductive layer is formed of a metal, wherein an oxide of said metal is conductive.
 13. The method of claim 11, wherein said first conductive layer is formed of a material selected from the group consisting of Ru, RuO₂, Ir, IrO₂, Ta, Rh, RhO_(x), VO₃, a Pt—Ru alloy and a Pt—Rh alloy.
 14. The method of claim 11 further comprising forming a barrier layer in contact with and beneath at a portion of said first conductive layer.
 15. The method of claim 11, wherein said second conductive layer is formed of material selected from the group consisting of hemispherical grained polysilicon, silica, silicon, germanium and alloys of silica and germanium.
 16. The method of claim 11 further comprising forming a third conductive layer between said first conductive layer and said first dielectric layer.
 17. The method of claim 16, wherein said third conductive layer is formed of a material selected from the group consisting of hemispherical grained polysilicon, silica, silicon, germanium and alloys of silica and germanium.
 18. The method of claim 11, wherein said first dielectric layer is a nitride film formed by rapid thermal nitridation (RTN).
 19. The method of claim 11, wherein said second dielectric layer is formed of a material selected from the group consisting of Ta₂O₅, SrTiO₃, Y₂O₃, Nb₂O₅, ZrO₂ and TiO_(x).
 20. The method of claim 11, wherein said pair of memory cells is a pair of DRAM memory cells. 